NY-A2/NY-A2P
Tg170℃ Lead-free Compatible
Excellent Peel Strength
Very Low Z-axis CTE
Excellent Anti-CAF Performance
UV Blocking/AOI Compatible
Low Water Absorption
Excellent Dimension Stability
-
Automotive
Typical Properties for NY-A2 Laminate
| 属性 Property | 项目 Item | 测试方法 IPC-TM-650 | 测试条件 Test Condition | 单位 Unit | 典型值 Typical Value | |
| 热性能 Thermal | 玻璃态转换温度 Tg Glass Transition Temperature | 2.4.25 | DSC | ℃ | \ | |
| 2.4.24 | TMA | ℃ | 170 | |||
| 2.4.24.4 | DMA | ℃ | 240 | |||
| X/Y轴热膨胀系数 X/Y-axis CTE | 2.4.24.5 | ＜Tg,TMA | ppm/°C | 13\14 | ||
| Z轴热膨胀系数 Z-axis CTE | 2.4.24 | ＜Tg,TMA | ppm/°C | 35 | ||
| ＞Tg,TMA | ppm/°C | 170 | ||||
| 2.4.24 | 50~260℃ | % | 1.8 | |||
| 热分解温度 Td Decomposition Temperature | 2.4.24.6 | TGA(5%W.L) | ℃ | 350 | ||
| 耐热性 T288 Thermal Resistance | 2.4.24.1 | Clad | Min | 35 | ||
| Etched | Min | 50 | ||||
| 电性能 Electrical | 介电常数 Dk (R/C:55%/70%) Permittivity | 1MHz | 2.5.5.9 | C-24/23/50 | — | 4.50/4.05 |
| 1GHz | 4.45/4.00 | |||||
| 10GHz | SPDR method | \ | ||||
| 介质损耗 Df (R/C:55%/70%) Loss Tangent | 1MHz | 2.5.5.9 | C-24/23/50 | — | 0.0156\0.0167 | |
| 1GHz | — | 0.0167\0.0179 | ||||
| 10GHz | SPDR method | \ | ||||
| 体积电阻 Volume Resistivity | 2.5.17.1 | C-96/35/90 | MΩ-cm | 2.8×108 | ||
| 表面电阻 Surface Resistivity | MΩ | 2.5×107 | ||||
| 物理性能 Physical | 吸水率 Water Absorption | 2.6.2.1 | E-1/105+D-24/23 | % | 0.08 | |
| 剥离强度 (HTE) Peel Strength | 1oz | 2.4.8 | As Received | N/mm | 1 | |
| 剥离强度(RTF) Peel Strength | 1oz | \ | ||||
| 剥离强度(HVLP) Peel Strength | 1oz | \ | ||||
| 弯曲强度 Flexural Strength | Warp | 2.4.4 | As Received | N/mm2 | 580 | |
| Fill | 460 | |||||
| 耐燃性 Flame Resistance | UL-94 | A&E-4/125 | — | V-0 | ||